Сварочная проволока из нержавеющей стали ER316L

ER3016L is austenite extra-low carbon stainless steel MIG wire. its weld metal has good anticorrosion to acetic acid, phosphoric acid, sulphurous acid, salt, particularly anticorrosion to chloridion and it has good performance of heat-resisting and crack-resisting. It is mainly used for welding structures in chemical industry or in power engineering projects that fabricated by stainless steel AISI316, SUS316. Also it can be used for welding high chromium steels that could not be PWHT or for dissimilar steels welding.

Welding Position: F, H, HF, OH, V

Type of Current: DCEP

Notices:

• Keeping the package of the wire in good condition before welding.
• To avoid welding defects the shield gas should be pure particularly no moisture in it.
• The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on.
• The flowrate of the shield gas should be 20L-25L/minute and arc length in welding should be 4mm-6mm.
• Mechanical properties, crack resistance and appearance of the weld metal are affected by heat input in welding so should pay more attention to it.
• The welding conditions mentioned above for reference only and it is better to do a welding procedure qualification according to project before put it into formal welding.

ER316L Chemical Composition of Deposited Metal (%)

	C	MN	SI	S	P	NI	CR	MO	CU
Standard	≤0.03	1.0-2.5	0.30-0.65	≤0.03	≤0.03	11.0-14.0	18.0-20.0	2.0-3.0	≤0.75
Typical	0.025	2.05	0.48	0.009	0.018	11.5	18.54	2.18	0.07

Mechanical Properties of Deposited Metal (AW)

	TENSILE STRENGTH RM (MPA)	ELONGATION A4 (%)
Standard	≥490	≥30
Typical	570	34

---

Если вам нужна консультация по цене, пожалуйста, свяжитесь с бизнес - отделом по электронной почте: